ABSTRACT
Objective: To evaluate if alcoholic beverages can cause color change in composite resins, if the alcoholic concentration influences this variation besides analyzing within the composite resins tested, which would present greater color stability when subjected to the experiment. Material and Methods: 90 specimens of three different composite resins (IPS Empress Direct, Grandio®So and Filtek Z350 XT) were immersed in distilled water (control group), red wine and vodka. The samples were 2 mm thick and 8 mm in diameter, photopolymerized for 20 s on each side, polished with sandpaper, silicon carbide tip and felt disc with prophylactic paste and immersed in distilled water at 37 °C for 24 h prior to subgrouping. For the evaluation of the color variation, the formula prioritized by the CIEL *a *b* system was used. Data were analyzed by ANOVA and Tukey's test at 95% significance. Results: The lowest variations occurred with the Grandio®So resin when exposed to wine, and Filtek Z350 XT when exposed to vodka. There was a statistically significant difference between the groups in water (p < 0.01) and in red wine (p < 0.01), but not in vodka (p > 0.05). The soaking medium that most caused staining was red wine. Conclusion: Red wine was the drink that generated the highest staining in all the resins tested, vodka did not change color stability significantly, the alcoholic concentrations tested did not directly influence the color change and the composite resin Grandio®So presented greater color stability when exposed to red wine. (AU)
Objetivo: Avaliar se bebidas alcóolicas podem provocar alteração de cor em resinas compostas, se a concentração alcóolica tem influência nesta variação além de analisar dentre as resinas compostas testadas, qual apresentaria maior estabilidade de cor quando submetidas ao experimento. Material e métodos: Foram confeccionados 90 espécimes de 3 diferentes resinas compostas (IPS Empress Direct, Grandio®So e Filtek Z350 XT) e imersos em água destilada (grupo controle), vinho tinto e vodca. As amostras mediam 2 mm de espessura e 8 mm de diâmetro, foram fotopolimerizados por 20 s cada lado, polidos com disco de lixa, ponta de carbeto de silício e disco de feltro com pasta profilática e imersos em água destilada a 37 ºC por 24 h antes da divisão em subgrupos. Para a avaliação da variação de cor foi utilizada a fórmula priorizada pelo sistema CIEL*a*b*. Os dados foram analisados por ANOVA e teste de Tukey a 95% de significância. Resultados: As menores variações ocorreram com a resina Grandio®So quando exposta ao vinho, e a Filtek Z350 XT quando exposta à vodca. Houve diferença estatisticamente significante entre os grupos na água (p < 0.01) e no vinho tinto (p < 0.01), mas não na vodca (p > 0,05). O meio de imersão que mais causou manchamento foi o vinho tinto. Conclusão: O vinho tinto foi a bebida que gerou o maior manchamento em todas as resinas testadas, a vodca não alterou a estabilidade de cor de maneira significativa, as concentrações alcóolicas testadas não influenciaram diretamente na alteração de cor e a resina composta Grandio®So apresentou maior estabilidade de cor frente ao vinho tinto. (AU)
Subject(s)
Alcoholic Beverages , Color , Composite Resins , Dental Materials , Resin CementsABSTRACT
Para analisar a capacidade de selamento marginal de três sistemas adesivos com diferentes formas de tratamentos superficiais, foram selecionados 45 incisivos bovinos, íntegros e recém-extraídos. Cada dente recebeu um preparo cavitário Classe V no limite cemento-esmalte. Os preparos foram padronizados nas seguintes dimensões: 1,5mm de profundidade e 2,0mm de diâmetro. A margem incisal foi deixada em esmalte e a margem gengival localizada abaixo da junção cemento-esmalte. Os dentes foram divididos em três grupos com 15 dentes cada. No grupo I foi utilizado o Adesivo XP Bond com dentina deixada úmida após condicionamento ácido. O grupo II também teve aplicação do Adesivo XP Bond, sendo que a dentina foi seca após condicionamento ácido. No grupo III o sistema utilizado foi o Adper Single-Bond 2. Todos os dentes foram restaurados com resina composta nanoparticulada Filtek - Z350 (3M). Em seguida foi realizada a ciclagem térmica em 300 ciclos, e os dentes foram imersos em solução aquosa de azul de metileno 2% por um período de 3 horas. Para avaliação do grau de penetração do corante, foram determinados escores de 0 a 3. A análise da penetração do corante foi realizada e o teste Kruskal-Wallis ao nível de significância de 5% foi aplicado. Em esmalte e em dentina houve diferença entre os grupos, porém a infiltração foi maior na dentina do que no esmalte.
Subject(s)
Animals , Composite Resins , Dental Enamel , Dentin , Dental CementumABSTRACT
Para analisar a capacidade de selamento marginal de três sistemas adesivos com formas diferentes de tratamentos superficiais foram selecionados 45 incisivos bovinos, íntegros e recém extraídos. Cada dente recebeu um preparo cavitáriode Classe V no limite cemento-esmalte. Os preparos foram padronizados nas seguintes dimensões: 1,5mm de profundidade e 2,0mm de diâmetro. A margem incisal foi deixada em esmalte e a margem gengival localizada abaixo da junção cemento-esmalte. Os dentes foram divididos em três grupos com 15 dentes cada. No grupo I foi utilizado oAdesivo XP Bond com dentina deixada úmida após condicionamento ácido. No grupo II o sistema utilizado foi o AdperSE Plus e no grupo lll foi aplicado o sistema adesivo Adper Single-Bond 2. Em seguida, os dentes foram restaurados com resina composta nanoparticulada Filtek Z350 (3M). Após ciclagem térmica (300 ciclos), os dentes foram imersos em solução aquosa de Azul de Metileno 2% por um período de 3 horas. Para avaliação do grau de penetração do corante foram determinados escores de 0 a 3. A análise da penetração do corante foi realizada através de microscopia óptica e aplicado o teste Kruskal-Wallis ao nível de significância de 5%. Em esmalte e dentina houve diferença entre os grupos, porém a infiltração foi maior na dentina que em esmalte, com exceção do sistema auto condicionante.
To evaluate the marginal sealing capacity of three adhesive systems with different forms of superficial treatments, 45 complete and just extracted bovine teeth were selected. Class V cavities (1,5mm of depth and 2,0mm of diameter) were prepared in all teeth in the cement-enamel junction. The incisal edge was left in enamel and the gingival edge located below of the cement-enamel junction. The teeth were divided into three groups with 15 teeth each. In group I, after the acid etching, Adhesive XP Bond was used with humid dentin. In the group II, the Adper SE Plus system was used, and in group III the adhesive system Adper Single-Bond 2 was applied. After that, the teeth had been filled with composite resin Filtek Z 350(3M). After the termocicled (300 cycles varying from 5 to 55°C), the teeth were immersed in 2% methylene blue solution for 3 hours. The degree of penetration of methylene blue they was evaluated by scores. The analysis of the penetration was carried through optic microscopy and Kruskal-Wallis test was apllied (á= 5%). There was difference among groups regarding sealing capacity. Infiltration was greater in dentine than enamel, with exceptionof the self-etch adhesive system.
Subject(s)
Dental Cements , Dentin , Dental Enamel , Dental Leakage , Dental Cavity PreparationABSTRACT
A infiltração marginal é um dos grandes desafios da Odontologia Restauradora, principalmente em restaurações deresina composta. A proposta desse estudo foi avaliar a capacidade de selamento marginal de restaurações de resina composta, com duas formas de cavidade e diferentes métodos para acabamento da margem em esmalte: instrumentos manuais, rotatórios e laseres de Er:YAG e Nd:YAG. Para isso foram utilizados 100 incisivos bovinos, recém-extraídos, e preparadas 200 cavidades nas faces proximais, com margem cervical em esmalte. Em seguida os dentes foram divididosem 10 grupos, onde se variou a forma da cavidade (caixa e arredondada) e os métodos de acabamento (instrumentosmanual, rotatório e laseres de Er:YAG e Nd:YAG). Após o preparo cavitário e o acabamento marginal, as cavidades foram restauradas com resina composta pela técnica incremental. Os espécimes foram impermeabilizados com esmalte para unhas, excetuando-se 1,0mm ao redor das restaurações, termociclados em 500 ciclos, variando de 5 a 55oC e imersos em solução de nitrato de prata a 50% por 24 horas. Os dentes foram seccionados e os cortes analisados em microscopia ótica, fotografados e a microinfiltração mensurada. Para análise dos resultados foram utilizados os testes ANOVA One-Way eKruskal-Wallis. Os resultados mostraram que o melhor acabamento marginal realizado foi com o laser de Er:YAG, tanto nas cavidades arredondadas como naquelas em forma de caixa; o laser de Nd:YAG apresentou a maior microinfiltração nas cavidades em forma de caixa. Quando comparado os dois tipos de cavidade, as arredondadas apresentaram menorinfiltração marginal para todas as formas de acabamento.
Marginal leakage is one of the great challenges of restorative dentistry, mainly in composite resin restorations. The purpose of this study was to evaluated the sealing capacity of composite resin fillings, with two cavities forms and differentmethods for finishing of the enamel edge: manual and rotatory instruments, Er:YAG and Nd:YAG lasers. For this 100bovine, just-extracted teeth were used, where 200 class II cavity were prepared, with the cervical edge in enamel. After that the teeth were divided in 10 groups, where if it varied the cavity form and methods of finishing. After cavity prepare and the marginal finishing, the cavities were filled with composite resin for the incremental technique. The specimens were painted with nail polish, excepting themselves 1,0mm around of the restorations, termocicled in 500 cycles varyingof 5-55oC and immersed in 50% silver nitrate solution for 24 hours. The teeth were sectioned and the cuts analyzedin optical microcopy, photographed and the microleakage was measured. The ANOVA One-Way and Kruskal-Wallisstatistical tests were used. The results showed that the best marginal finishing was with the laser of Er:YAG, as muchin the rounded cavity off as in the ones in box form. The Nd:YAG laser presented biggest microleakage in box form cavities. When compared the two types of cavities, the rounded presented the smallest leakage who the box form, for all the finishing forms.
Subject(s)
Animals , Cattle , Dental Enamel , Dental Leakage , Dental Marginal Adaptation , Dental Polishing , Dental Restoration, Permanent/instrumentationABSTRACT
O selamento marginal constituiu-se em um dos principais obstáculos para as restaurações adesivas, principalmente quando novos tratamentos são propostos para esmalte e/ou dentina. Este estudo tem por finalidade analisar a capacidade de selamento marginal de dois sistemas adesivos atuais, um com primer autocondicionante (Clearfil Liner Bond 2V) e o outro com condicionamento ácido total (Excite), e comparar a performance dos mesmos em dentes humanos e bovinos, frente ao teste de microinfiltração. Para isto, foram utilizados vinte terceiros molares humanos e vinte incisivos bovinos. Foram preparadas cavidades de classe V em todos os dentes que após a aplicação dos sistemas adesivos foram restauradas com resina composta. Os espécimes foram impermeabilizados com esmalte para unhas, com exceção de 1,0mm ao redor das restaurações, termociclados (300 ciclos variando de 5°a 55°C) e imersos em solução de nitrato de prata a 50 por cento por 24 horas. Após análise da microinfiltração em lupa estereoscópica e teste estatístico de Kruskall-Wallis ao nível de significância de 5 por cento, constatou-se que o sistema adesivo Excite apresentou a maior infiltração em esmalte de dentes bovinos, Clearfil foi o que melhor selou a mergem gengival em dentes humanos e bovinos; dentes humanos e bovinos se comportaram de maneira semelhante frente ao Excite, porém em relação ao Clearfil houve diferença estatisticamente significante